A413.0 Aluminum vs. EN-MC21110 Magnesium
A413.0 aluminum belongs to the aluminum alloys classification, while EN-MC21110 magnesium belongs to the magnesium alloys.
For each property being compared, the top bar is A413.0 aluminum and the bottom bar is EN-MC21110 magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 80 | |
| 58 to 63 |
| Elastic (Young's, Tensile) Modulus, GPa | 73 | |
| 46 |
| Elongation at Break, % | 3.5 | |
| 2.8 to 6.7 |
| Fatigue Strength, MPa | 130 | |
| 75 to 78 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 27 | |
| 18 |
| Shear Strength, MPa | 170 | |
| 120 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 240 | |
| 200 to 270 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 100 to 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 570 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 130 |
| Melting Completion (Liquidus), °C | 590 | |
| 600 |
| Melting Onset (Solidus), °C | 580 | |
| 500 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 990 |
| Thermal Conductivity, W/m-K | 120 | |
| 80 |
| Thermal Expansion, µm/m-K | 21 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 31 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 61 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 12 |
| Density, g/cm3 | 2.6 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 7.6 | |
| 23 |
| Embodied Energy, MJ/kg | 140 | |
| 160 |
| Embodied Water, L/kg | 1040 | |
| 990 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 7.1 | |
| 4.9 to 14 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 | |
| 120 to 150 |
| Stiffness to Weight: Axial, points | 16 | |
| 15 |
| Stiffness to Weight: Bending, points | 54 | |
| 69 |
| Strength to Weight: Axial, points | 25 | |
| 33 to 44 |
| Strength to Weight: Bending, points | 33 | |
| 45 to 54 |
| Thermal Diffusivity, mm2/s | 52 | |
| 47 |
| Thermal Shock Resistance, points | 11 | |
| 12 to 16 |
Alloy Composition
| Aluminum (Al), % | 82.9 to 89 | |
| 7.0 to 8.7 |
| Copper (Cu), % | 0 to 1.0 | |
| 0 to 0.030 |
| Iron (Fe), % | 0 to 1.3 | |
| 0 to 0.0050 |
| Magnesium (Mg), % | 0 to 0.1 | |
| 89.6 to 92.6 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0.1 to 0.35 |
| Nickel (Ni), % | 0 to 0.5 | |
| 0 to 0.0020 |
| Silicon (Si), % | 11 to 13 | |
| 0 to 0.2 |
| Tin (Sn), % | 0 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0.35 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.010 |