ACI-ASTM CA15 Steel vs. EN 1.4305 Stainless Steel

Both ACI-ASTM CA15 steel and EN 1.4305 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA15 steel and the bottom bar is EN 1.4305 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
200 to 270
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 21
14 to 40
Fatigue Strength, MPa 370
190 to 330
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 700
610 to 900
Tensile Strength: Yield (Proof), MPa 570
220 to 570

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 390
410
Maximum Temperature: Mechanical, °C 750
930
Melting Completion (Liquidus), °C 1440
1420
Melting Onset (Solidus), °C 1500
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 25
15
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.0
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.5
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
15
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.0
3.0
Embodied Energy, MJ/kg 28
42
Embodied Water, L/kg 100
140

Common Calculations

PREN (Pitting Resistance) 14
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
110 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 820
120 to 830
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 25
22 to 32
Strength to Weight: Bending, points 23
20 to 27
Thermal Diffusivity, mm2/s 6.7
4.0
Thermal Shock Resistance, points 26
14 to 20

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.1
Chromium (Cr), % 11.5 to 14
17 to 19
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 81.8 to 88.5
66.4 to 74.9
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 0 to 1.0
8.0 to 10
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.040
0.15 to 0.35