ACI-ASTM CK3MCuN Steel vs. SAE-AISI 1025 Steel

Both ACI-ASTM CK3MCuN steel and SAE-AISI 1025 steel are iron alloys. They have 53% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK3MCuN steel and the bottom bar is SAE-AISI 1025 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
130 to 140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
17 to 28
Fatigue Strength, MPa 250
190 to 280
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 620
450 to 500
Tensile Strength: Yield (Proof), MPa 290
250 to 420

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1090
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1350
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 12
52
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 29
1.8
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.6
1.4
Embodied Energy, MJ/kg 76
18
Embodied Water, L/kg 190
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
80 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 210
170 to 470
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
16 to 18
Strength to Weight: Bending, points 20
17 to 18
Thermal Diffusivity, mm2/s 3.2
14
Thermal Shock Resistance, points 14
14 to 16

Alloy Composition

Carbon (C), % 0 to 0.025
0.22 to 0.28
Chromium (Cr), % 19.5 to 20.5
0
Copper (Cu), % 0.5 to 1.0
0
Iron (Fe), % 49.5 to 56.3
99.03 to 99.48
Manganese (Mn), % 0 to 1.2
0.3 to 0.6
Molybdenum (Mo), % 6.0 to 7.0
0
Nickel (Ni), % 17.5 to 19.5
0
Nitrogen (N), % 0.18 to 0.24
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.010
0 to 0.050