ACI-ASTM CK3MCuN Steel vs. SAE-AISI 9260 Steel
Both ACI-ASTM CK3MCuN steel and SAE-AISI 9260 steel are iron alloys. They have 54% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CK3MCuN steel and the bottom bar is SAE-AISI 9260 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 | |
| 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 39 | |
| 21 |
| Fatigue Strength, MPa | 250 | |
| 260 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 80 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 660 |
| Tensile Strength: Yield (Proof), MPa | 290 | |
| 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 1090 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1430 |
| Melting Onset (Solidus), °C | 1350 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 480 |
| Thermal Conductivity, W/m-K | 12 | |
| 45 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.9 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 2.0 |
| Density, g/cm3 | 8.0 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 5.6 | |
| 1.5 |
| Embodied Energy, MJ/kg | 76 | |
| 20 |
| Embodied Water, L/kg | 190 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 | |
| 380 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 21 | |
| 24 |
| Strength to Weight: Bending, points | 20 | |
| 22 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 12 |
| Thermal Shock Resistance, points | 14 | |
| 20 |
Alloy Composition
| Carbon (C), % | 0 to 0.025 | |
| 0.56 to 0.64 |
| Chromium (Cr), % | 19.5 to 20.5 | |
| 0 |
| Copper (Cu), % | 0.5 to 1.0 | |
| 0 |
| Iron (Fe), % | 49.5 to 56.3 | |
| 96.1 to 96.9 |
| Manganese (Mn), % | 0 to 1.2 | |
| 0.75 to 1.0 |
| Molybdenum (Mo), % | 6.0 to 7.0 | |
| 0 |
| Nickel (Ni), % | 17.5 to 19.5 | |
| 0 |
| Nitrogen (N), % | 0.18 to 0.24 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 1.0 | |
| 1.8 to 2.2 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.040 |