AISI 204 Stainless Steel vs. SAE-AISI 9310 Steel

Both AISI 204 stainless steel and SAE-AISI 9310 steel are iron alloys. They have 77% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 204 stainless steel and the bottom bar is SAE-AISI 9310 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 330
540 to 610
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 23 to 39
17 to 19
Fatigue Strength, MPa 320 to 720
300 to 390
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 500 to 700
510 to 570
Tensile Strength: Ultimate (UTS), MPa 730 to 1100
820 to 910
Tensile Strength: Yield (Proof), MPa 380 to 1080
450 to 570

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 850
440
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
48
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 10
4.4
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.4
1.8
Embodied Energy, MJ/kg 35
24
Embodied Water, L/kg 130
57

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240 to 250
120 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 360 to 2940
540 to 860
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27 to 40
29 to 32
Strength to Weight: Bending, points 24 to 31
25 to 27
Thermal Diffusivity, mm2/s 4.1
13
Thermal Shock Resistance, points 16 to 24
24 to 27

Alloy Composition

Carbon (C), % 0 to 0.030
0.080 to 0.13
Chromium (Cr), % 15 to 17
1.0 to 1.4
Iron (Fe), % 69.6 to 76.4
93.8 to 95.2
Manganese (Mn), % 7.0 to 9.0
0.45 to 0.65
Molybdenum (Mo), % 0
0.080 to 0.15
Nickel (Ni), % 1.5 to 3.0
3.0 to 3.5
Nitrogen (N), % 0.15 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 0 to 1.0
0.2 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.012