AISI 304N Stainless Steel vs. Monel 400
AISI 304N stainless steel belongs to the iron alloys classification, while Monel 400 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AISI 304N stainless steel and the bottom bar is Monel 400.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 160 |
| Elongation at Break, % | 9.1 to 45 | |
| 20 to 40 |
| Fatigue Strength, MPa | 220 to 440 | |
| 230 to 290 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 77 | |
| 62 |
| Shear Strength, MPa | 420 to 700 | |
| 370 to 490 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 1180 | |
| 540 to 780 |
| Tensile Strength: Yield (Proof), MPa | 270 to 850 | |
| 210 to 590 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 960 | |
| 1000 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1350 |
| Melting Onset (Solidus), °C | 1380 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 430 |
| Thermal Conductivity, W/m-K | 16 | |
| 23 |
| Thermal Expansion, µm/m-K | 16 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 3.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 3.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 50 |
| Density, g/cm3 | 7.8 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 7.9 |
| Embodied Energy, MJ/kg | 43 | |
| 110 |
| Embodied Water, L/kg | 150 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 98 to 280 | |
| 140 to 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 1830 | |
| 140 to 1080 |
| Stiffness to Weight: Axial, points | 14 | |
| 10 |
| Stiffness to Weight: Bending, points | 25 | |
| 21 |
| Strength to Weight: Axial, points | 22 to 42 | |
| 17 to 25 |
| Strength to Weight: Bending, points | 21 to 32 | |
| 17 to 21 |
| Thermal Diffusivity, mm2/s | 4.2 | |
| 6.1 |
| Thermal Shock Resistance, points | 14 to 26 | |
| 17 to 25 |
Alloy Composition
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.3 |
| Chromium (Cr), % | 18 to 20 | |
| 0 |
| Copper (Cu), % | 0 | |
| 28 to 34 |
| Iron (Fe), % | 66.4 to 73.9 | |
| 0 to 2.5 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 2.0 |
| Nickel (Ni), % | 8.0 to 10.5 | |
| 63 to 72 |
| Nitrogen (N), % | 0.1 to 0.16 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.024 |