AISI 308L Stainless Steel vs. EN 1.0034 Steel

Both AISI 308L stainless steel and EN 1.0034 steel are iron alloys. They have 68% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 308L stainless steel and the bottom bar is EN 1.0034 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
97 to 110
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
9.0 to 32
Fatigue Strength, MPa 180
140 to 170
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 380
220 to 230
Tensile Strength: Ultimate (UTS), MPa 580
340 to 380
Tensile Strength: Yield (Proof), MPa 230
180 to 280

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1010
400
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
53
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 16
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.2
1.4
Embodied Energy, MJ/kg 45
18
Embodied Water, L/kg 160
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
31 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 140
84 to 210
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
12 to 13
Strength to Weight: Bending, points 20
14 to 15
Thermal Diffusivity, mm2/s 4.1
14
Thermal Shock Resistance, points 13
11 to 12

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.15
Chromium (Cr), % 19.5 to 22
0
Iron (Fe), % 63.8 to 70.5
98.7 to 100
Manganese (Mn), % 1.0 to 2.5
0 to 0.7
Nickel (Ni), % 9.0 to 11
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0.25 to 0.6
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.045