AISI 316LN Stainless Steel vs. S31655 Stainless Steel

Both AISI 316LN stainless steel and S31655 stainless steel are iron alloys. Both are furnished in the annealed condition. They have a very high 95% of their average alloy composition in common. There are 34 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 316LN stainless steel and the bottom bar is S31655 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
210
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 42
39
Fatigue Strength, MPa 200
300
Poisson's Ratio 0.28
0.28
Rockwell B Hardness 80
88
Shear Modulus, GPa 82
78
Shear Strength, MPa 410
490
Tensile Strength: Ultimate (UTS), MPa 590
710
Tensile Strength: Yield (Proof), MPa 230
350

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 410
430
Maximum Temperature: Mechanical, °C 940
1010
Melting Completion (Liquidus), °C 1450
1430
Melting Onset (Solidus), °C 1380
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 19
17
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.8
3.3
Embodied Energy, MJ/kg 53
46
Embodied Water, L/kg 150
160

Common Calculations

PREN (Pitting Resistance) 27
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
230
Resilience: Unit (Modulus of Resilience), kJ/m3 130
310
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
25
Strength to Weight: Bending, points 20
23
Thermal Diffusivity, mm2/s 4.1
4.0
Thermal Shock Resistance, points 13
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 16 to 18
19.5 to 21.5
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 62 to 71.9
63.2 to 71.9
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
0.5 to 1.5
Nickel (Ni), % 10 to 14
8.0 to 9.5
Nitrogen (N), % 0.1 to 0.16
0.14 to 0.25
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015