AISI 415 Stainless Steel vs. EN 1.4470 Stainless Steel

Both AISI 415 stainless steel and EN 1.4470 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 415 stainless steel and the bottom bar is EN 1.4470 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
23
Fatigue Strength, MPa 430
320
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
80
Tensile Strength: Ultimate (UTS), MPa 900
680
Tensile Strength: Yield (Proof), MPa 700
480

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Maximum Temperature: Corrosion, °C 390
430
Maximum Temperature: Mechanical, °C 780
1060
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 24
18
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.1
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 11
17
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.5
3.6
Embodied Energy, MJ/kg 35
49
Embodied Water, L/kg 110
160

Common Calculations

PREN (Pitting Resistance) 15
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
140
Resilience: Unit (Modulus of Resilience), kJ/m3 1250
570
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 32
24
Strength to Weight: Bending, points 26
22
Thermal Diffusivity, mm2/s 6.4
4.8
Thermal Shock Resistance, points 33
18

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.030
Chromium (Cr), % 11.5 to 14
21 to 23
Iron (Fe), % 77.8 to 84
63.7 to 71.9
Manganese (Mn), % 0.5 to 1.0
0 to 2.0
Molybdenum (Mo), % 0.5 to 1.0
2.5 to 3.5
Nickel (Ni), % 3.5 to 5.5
4.5 to 6.5
Nitrogen (N), % 0
0.12 to 0.2
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.025