ASTM A182 Grade F1 vs. SAE-AISI 1141 Steel
Both ASTM A182 grade F1 and SAE-AISI 1141 steel are iron alloys. They have a very high 99% of their average alloy composition in common.
For each property being compared, the top bar is ASTM A182 grade F1 and the bottom bar is SAE-AISI 1141 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 | |
| 210 to 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 22 | |
| 11 to 17 |
| Fatigue Strength, MPa | 220 | |
| 270 to 430 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 34 | |
| 34 to 39 |
| Shear Modulus, GPa | 73 | |
| 72 |
| Shear Strength, MPa | 340 | |
| 460 to 480 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 740 to 810 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 400 to 700 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 400 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 50 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 1.9 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.4 |
| Embodied Energy, MJ/kg | 20 | |
| 19 |
| Embodied Water, L/kg | 48 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 | |
| 86 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 430 to 1290 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 19 | |
| 26 to 29 |
| Strength to Weight: Bending, points | 19 | |
| 23 to 25 |
| Thermal Diffusivity, mm2/s | 13 | |
| 14 |
| Thermal Shock Resistance, points | 16 | |
| 24 to 26 |
Alloy Composition
| Carbon (C), % | 0 to 0.28 | |
| 0.37 to 0.45 |
| Iron (Fe), % | 97.7 to 98.8 | |
| 97.7 to 98.2 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 1.4 to 1.7 |
| Molybdenum (Mo), % | 0.44 to 0.65 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 |
| Sulfur (S), % | 0 to 0.045 | |
| 0.080 to 0.13 |