ASTM A182 Grade F1 vs. C15000 Copper
ASTM A182 grade F1 belongs to the iron alloys classification, while C15000 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F1 and the bottom bar is C15000 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 22 | |
| 13 to 54 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 43 |
| Shear Strength, MPa | 340 | |
| 150 to 280 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 200 to 460 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 45 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 200 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1080 |
| Melting Onset (Solidus), °C | 1420 | |
| 980 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 50 | |
| 370 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 93 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 93 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 31 |
| Density, g/cm3 | 7.9 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 2.7 |
| Embodied Energy, MJ/kg | 20 | |
| 43 |
| Embodied Water, L/kg | 48 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 | |
| 19 to 250 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 8.7 to 910 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 19 | |
| 6.2 to 14 |
| Strength to Weight: Bending, points | 19 | |
| 8.5 to 15 |
| Thermal Diffusivity, mm2/s | 13 | |
| 110 |
| Thermal Shock Resistance, points | 16 | |
| 7.3 to 17 |
Alloy Composition
| Carbon (C), % | 0 to 0.28 | |
| 0 |
| Copper (Cu), % | 0 | |
| 99.8 to 99.9 |
| Iron (Fe), % | 97.7 to 98.8 | |
| 0 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 |
| Molybdenum (Mo), % | 0.44 to 0.65 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 |
| Sulfur (S), % | 0 to 0.045 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0.1 to 0.2 |