ASTM A182 Grade F23 vs. 50Cr-50Ni-Cb Alloy
ASTM A182 grade F23 belongs to the iron alloys classification, while 50Cr-50Ni-Cb alloy belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F23 and the bottom bar is 50Cr-50Ni-Cb alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 22 | |
| 5.6 |
| Poisson's Ratio | 0.29 | |
| 0.26 |
| Shear Modulus, GPa | 74 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 350 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Expansion, µm/m-K | 13 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 60 |
| Density, g/cm3 | 8.0 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.5 | |
| 9.2 |
| Embodied Energy, MJ/kg | 36 | |
| 130 |
| Embodied Water, L/kg | 59 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 30 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 550 | |
| 370 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 20 | |
| 21 |
| Strength to Weight: Bending, points | 19 | |
| 20 |
| Thermal Shock Resistance, points | 17 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.030 | |
| 0 to 0.25 |
| Boron (B), % | 0.0010 to 0.0060 | |
| 0 |
| Carbon (C), % | 0.040 to 0.1 | |
| 0 to 0.1 |
| Chromium (Cr), % | 1.9 to 2.6 | |
| 47 to 52 |
| Iron (Fe), % | 93.2 to 96.2 | |
| 0 to 1.0 |
| Manganese (Mn), % | 0.1 to 0.6 | |
| 0 to 0.3 |
| Molybdenum (Mo), % | 0.050 to 0.3 | |
| 0 |
| Nickel (Ni), % | 0 to 0.4 | |
| 43.3 to 51.6 |
| Niobium (Nb), % | 0.020 to 0.080 | |
| 1.4 to 1.7 |
| Nitrogen (N), % | 0 to 0.015 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0.0050 to 0.060 | |
| 0 to 0.5 |
| Tungsten (W), % | 1.5 to 1.8 | |
| 0 |
| Vanadium (V), % | 0.2 to 0.3 | |
| 0 |