ASTM A182 Grade F3VCb vs. AWS BAg-13a
ASTM A182 grade F3VCb belongs to the iron alloys classification, while AWS BAg-13a belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F3VCb and the bottom bar is AWS BAg-13a.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 92 |
| Poisson's Ratio | 0.29 | |
| 0.36 |
| Shear Modulus, GPa | 74 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 670 | |
| 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 160 |
| Melting Completion (Liquidus), °C | 1470 | |
| 890 |
| Melting Onset (Solidus), °C | 1430 | |
| 770 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 300 |
| Thermal Expansion, µm/m-K | 13 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 9.8 |
| Embodied Carbon, kg CO2/kg material | 2.4 | |
| 54 |
| Embodied Energy, MJ/kg | 33 | |
| 850 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 5.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 15 |
| Strength to Weight: Axial, points | 24 | |
| 5.1 |
| Strength to Weight: Bending, points | 22 | |
| 7.2 |
| Thermal Shock Resistance, points | 19 | |
| 7.5 |
Alloy Composition
| Calcium (Ca), % | 0.00050 to 0.015 | |
| 0 |
| Carbon (C), % | 0.1 to 0.15 | |
| 0 |
| Chromium (Cr), % | 2.7 to 3.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 40.4 to 43.5 |
| Iron (Fe), % | 93.8 to 95.8 | |
| 0 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 0 |
| Nickel (Ni), % | 0 to 0.25 | |
| 1.5 to 2.5 |
| Niobium (Nb), % | 0.015 to 0.070 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Silver (Ag), % | 0 | |
| 55 to 57 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Titanium (Ti), % | 0 to 0.015 | |
| 0 |
| Vanadium (V), % | 0.2 to 0.3 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |