ASTM A182 Grade F3VCb vs. EN 1.4374 Stainless Steel

Both ASTM A182 grade F3VCb and EN 1.4374 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F3VCb and the bottom bar is EN 1.4374 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
230
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 21
40
Fatigue Strength, MPa 320
340
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
77
Shear Strength, MPa 420
550
Tensile Strength: Ultimate (UTS), MPa 670
800
Tensile Strength: Yield (Proof), MPa 460
400

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 470
920
Melting Completion (Liquidus), °C 1470
1400
Melting Onset (Solidus), °C 1430
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 4.5
14
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 2.4
2.9
Embodied Energy, MJ/kg 33
42
Embodied Water, L/kg 64
150

Common Calculations

PREN (Pitting Resistance) 6.3
23
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
270
Resilience: Unit (Modulus of Resilience), kJ/m3 570
400
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
29
Strength to Weight: Bending, points 22
25
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 19
17

Alloy Composition

Calcium (Ca), % 0.00050 to 0.015
0
Carbon (C), % 0.1 to 0.15
0.050 to 0.1
Chromium (Cr), % 2.7 to 3.3
17.5 to 18.5
Copper (Cu), % 0 to 0.25
0 to 0.4
Iron (Fe), % 93.8 to 95.8
63.5 to 67.9
Manganese (Mn), % 0.3 to 0.6
9.0 to 10
Molybdenum (Mo), % 0.9 to 1.1
0 to 0.5
Nickel (Ni), % 0 to 0.25
5.0 to 6.0
Niobium (Nb), % 0.015 to 0.070
0
Nitrogen (N), % 0
0.25 to 0.32
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.1
0.3 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.015
0
Vanadium (V), % 0.2 to 0.3
0