ASTM A182 Grade F92 vs. AWS ENi-1
ASTM A182 grade F92 belongs to the iron alloys classification, while AWS ENi-1 belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F92 and the bottom bar is AWS ENi-1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 180 |
| Elongation at Break, % | 22 | |
| 22 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 76 | |
| 69 |
| Tensile Strength: Ultimate (UTS), MPa | 690 | |
| 470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 310 |
| Melting Completion (Liquidus), °C | 1490 | |
| 1360 |
| Melting Onset (Solidus), °C | 1450 | |
| 1310 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 26 | |
| 73 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.3 | |
| 19 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 19 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 60 |
| Density, g/cm3 | 7.9 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 11 |
| Embodied Energy, MJ/kg | 40 | |
| 150 |
| Embodied Water, L/kg | 89 | |
| 230 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 12 |
| Stiffness to Weight: Bending, points | 24 | |
| 22 |
| Strength to Weight: Axial, points | 24 | |
| 15 |
| Strength to Weight: Bending, points | 22 | |
| 15 |
| Thermal Diffusivity, mm2/s | 6.9 | |
| 19 |
| Thermal Shock Resistance, points | 19 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.020 | |
| 0 to 1.0 |
| Boron (B), % | 0.0010 to 0.0060 | |
| 0 |
| Carbon (C), % | 0.070 to 0.13 | |
| 0 to 0.1 |
| Chromium (Cr), % | 8.5 to 9.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 85.8 to 89.1 | |
| 0 to 0.75 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0 to 0.75 |
| Molybdenum (Mo), % | 0.3 to 0.6 | |
| 0 |
| Nickel (Ni), % | 0 to 0.4 | |
| 92 to 99 |
| Niobium (Nb), % | 0.040 to 0.090 | |
| 0 |
| Nitrogen (N), % | 0.030 to 0.070 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.3 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 to 0.010 | |
| 1.0 to 4.0 |
| Tungsten (W), % | 1.5 to 2.0 | |
| 0 |
| Vanadium (V), % | 0.15 to 0.25 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |