ASTM A210 Steel vs. EN 1.4301 Stainless Steel
Both ASTM A210 steel and EN 1.4301 stainless steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A210 steel and the bottom bar is EN 1.4301 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 to 160 | |
| 190 to 270 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 34 | |
| 14 to 46 |
| Fatigue Strength, MPa | 230 to 250 | |
| 200 to 330 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 77 |
| Shear Strength, MPa | 320 to 360 | |
| 430 to 550 |
| Tensile Strength: Ultimate (UTS), MPa | 470 to 540 | |
| 610 to 900 |
| Tensile Strength: Yield (Proof), MPa | 290 to 310 | |
| 220 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 940 |
| Melting Completion (Liquidus), °C | 1460 to 1470 | |
| 1430 |
| Melting Onset (Solidus), °C | 1420 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 52 to 53 | |
| 15 |
| Thermal Expansion, µm/m-K | 12 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 to 8.1 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 15 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.0 |
| Embodied Energy, MJ/kg | 18 | |
| 43 |
| Embodied Water, L/kg | 45 to 46 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 160 | |
| 110 to 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 to 250 | |
| 120 to 820 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 17 to 19 | |
| 22 to 32 |
| Strength to Weight: Bending, points | 17 to 19 | |
| 20 to 27 |
| Thermal Diffusivity, mm2/s | 14 | |
| 4.0 |
| Thermal Shock Resistance, points | 15 to 17 | |
| 14 to 20 |