ASTM A217 Cast Steel vs. Grade 364 Molybdenum
ASTM A217 cast steel belongs to the iron alloys classification, while grade 364 molybdenum belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is ASTM A217 cast steel and the bottom bar is grade 364 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 310 |
| Elongation at Break, % | 21 to 27 | |
| 6.2 to 11 |
| Poisson's Ratio | 0.28 to 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 73 to 75 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 710 | |
| 580 to 720 |
| Tensile Strength: Yield (Proof), MPa | 270 to 460 | |
| 350 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 to 270 | |
| 370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 250 |
| Thermal Expansion, µm/m-K | 13 | |
| 7.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 2.1 | |
| 28 |
| Embodied Energy, MJ/kg | 20 to 28 | |
| 330 |
| Embodied Water, L/kg | 47 to 87 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 130 | |
| 43 to 57 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 570 | |
| 200 to 630 |
| Stiffness to Weight: Axial, points | 13 to 14 | |
| 17 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 22 |
| Strength to Weight: Axial, points | 19 to 25 | |
| 16 to 20 |
| Strength to Weight: Bending, points | 19 to 23 | |
| 15 to 17 |
| Thermal Shock Resistance, points | 16 to 20 | |
| 19 to 24 |