Grade 364 Molybdenum
Grade 364 molybdenum is a molybdenum alloy. It can have a moderately high tensile strength among the alloys in the same category in the database.
The properties of grade 364 molybdenum include two common variations. This page shows summary ranges across both of them. For more specific values, follow the links immediately below. The graph bars on the material properties cards further below compare grade 364 molybdenum to: molybdenum alloys (top), all alloys in the same category (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
310 GPa 45 x 106 psi
Elongation at Break
6.2 to 11 %
Poisson's Ratio
0.31
Shear Modulus
120 GPa 17 x 106 psi
Tensile Strength: Ultimate (UTS)
580 to 720 MPa 84 to 100 x 103 psi
Tensile Strength: Yield (Proof)
350 to 620 MPa 51 to 90 x 103 psi
Thermal Properties
Latent Heat of Fusion
370 J/g
Specific Heat Capacity
250 J/kg-K 0.060 BTU/lb-°F
Thermal Expansion
7.0 µm/m-K
Otherwise Unclassified Properties
Density
10 g/cm3 640 lb/ft3
Embodied Carbon
28 kg CO2/kg material
Embodied Energy
330 MJ/kg 140 x 103 BTU/lb
Embodied Water
360 L/kg 43 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
43 to 57 MJ/m3
Resilience: Unit (Modulus of Resilience)
200 to 630 kJ/m3
Stiffness to Weight: Axial
17 points
Stiffness to Weight: Bending
22 points
Strength to Weight: Axial
16 to 20 points
Strength to Weight: Bending
15 to 17 points
Thermal Shock Resistance
19 to 24 points
Alloy Composition
| Mo | 99.2 to 99.5 | |
| Ti | 0.4 to 0.55 | |
| Zr | 0.060 to 0.12 | |
| C | 0.010 to 0.040 | |
| O | 0 to 0.030 | |
| Fe | 0 to 0.010 | |
| Si | 0 to 0.0050 | |
| Ni | 0 to 0.0050 | |
| N | 0 to 0.0020 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Similar Alloys
Further Reading
ASTM B386: Standard Specification for Molybdenum and Molybdenum Alloy Plate, Sheet, Strip, and Foil
ASTM B387: Standard Specification for Molybdenum and Molybdenum Alloy Bar, Rod, and Wire
Sintering of Advanced Materials: Fundamentals and Processes, Zhigang Zak Fang (editor), 2010