ASTM A27 Cast Steel vs. EN 1.0308 Steel

Both ASTM A27 cast steel and EN 1.0308 steel are iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A27 cast steel and the bottom bar is EN 1.0308 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 25 to 27
7.8 to 28
Fatigue Strength, MPa 170 to 230
140 to 200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 460 to 550
360 to 440
Tensile Strength: Yield (Proof), MPa 230 to 310
190 to 340

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
51
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0 to 7.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18
18
Embodied Water, L/kg 45 to 46
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96 to 120
32 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 260
93 to 300
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16 to 20
13 to 16
Strength to Weight: Bending, points 17 to 19
14 to 16
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 15 to 18
11 to 14