ASTM A283 Carbon Steel vs. Grade 702C Zirconium
ASTM A283 carbon steel belongs to the iron alloys classification, while grade 702C zirconium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is ASTM A283 carbon steel and the bottom bar is grade 702C zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 110 to 140 | |
| 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 97 |
| Elongation at Break, % | 26 to 34 | |
| 13 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 360 to 480 | |
| 430 |
| Tensile Strength: Yield (Proof), MPa | 180 to 260 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 270 |
| Thermal Conductivity, W/m-K | 51 to 53 | |
| 22 |
| Thermal Expansion, µm/m-K | 12 | |
| 5.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 to 7.9 | |
| 6.7 |
| Embodied Water, L/kg | 46 | |
| 450 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 to 110 | |
| 52 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 91 to 180 | |
| 510 |
| Stiffness to Weight: Axial, points | 13 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 13 to 17 | |
| 18 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 19 |
| Thermal Diffusivity, mm2/s | 14 | |
| 12 |
| Thermal Shock Resistance, points | 11 to 15 | |
| 55 |