ASTM A285 Carbon Steel vs. Grade 23 Titanium
ASTM A285 carbon steel belongs to the iron alloys classification, while grade 23 titanium belongs to the titanium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A285 carbon steel and the bottom bar is grade 23 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 30 to 34 | |
| 6.7 to 11 |
| Fatigue Strength, MPa | 150 to 180 | |
| 470 to 500 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 73 | |
| 40 |
| Shear Strength, MPa | 250 to 290 | |
| 540 to 570 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 450 | |
| 930 to 940 |
| Tensile Strength: Yield (Proof), MPa | 190 to 230 | |
| 850 to 870 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 340 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1610 |
| Melting Onset (Solidus), °C | 1420 to 1430 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 560 |
| Thermal Conductivity, W/m-K | 53 | |
| 7.1 |
| Thermal Expansion, µm/m-K | 12 | |
| 9.4 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 1.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 2.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 36 |
| Density, g/cm3 | 7.9 | |
| 4.4 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 38 |
| Embodied Energy, MJ/kg | 18 | |
| 610 |
| Embodied Water, L/kg | 46 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 61 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 94 to 150 | |
| 3430 to 3560 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 35 |
| Strength to Weight: Axial, points | 13 to 16 | |
| 58 to 59 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 48 |
| Thermal Diffusivity, mm2/s | 14 | |
| 2.9 |
| Thermal Shock Resistance, points | 12 to 14 | |
| 67 to 68 |