ASTM A369 Grade FP2 vs. EN 1.4560 Stainless Steel

Both ASTM A369 grade FP2 and EN 1.4560 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP2 and the bottom bar is EN 1.4560 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
50
Fatigue Strength, MPa 160
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 270
390
Tensile Strength: Ultimate (UTS), MPa 430
550
Tensile Strength: Yield (Proof), MPa 240
190

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 420
940
Melting Completion (Liquidus), °C 1470
1420
Melting Onset (Solidus), °C 1430
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
15
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.6
3.0
Embodied Energy, MJ/kg 20
42
Embodied Water, L/kg 50
150

Common Calculations

PREN (Pitting Resistance) 2.5
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
220
Resilience: Unit (Modulus of Resilience), kJ/m3 150
92
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 15
20
Strength to Weight: Bending, points 16
19
Thermal Diffusivity, mm2/s 13
4.0
Thermal Shock Resistance, points 13
12

Alloy Composition

Carbon (C), % 0.1 to 0.2
0 to 0.035
Chromium (Cr), % 0.5 to 0.81
18 to 19
Copper (Cu), % 0
1.5 to 2.0
Iron (Fe), % 97.4 to 98.6
66.8 to 71
Manganese (Mn), % 0.3 to 0.61
1.5 to 2.0
Molybdenum (Mo), % 0.44 to 0.65
0
Nickel (Ni), % 0
8.0 to 9.0
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0.1 to 0.3
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015