ASTM A414 Steel vs. ACI-ASTM CK3MCuN Steel

Both ASTM A414 steel and ACI-ASTM CK3MCuN steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A414 steel and the bottom bar is ACI-ASTM CK3MCuN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110 to 180
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 15 to 26
39
Fatigue Strength, MPa 140 to 260
250
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 360 to 590
620
Tensile Strength: Yield (Proof), MPa 190 to 350
290

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1090
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1350
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 49 to 50
12
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2 to 7.3
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3 to 8.4
2.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
29
Density, g/cm3 7.8 to 7.9
8.0
Embodied Carbon, kg CO2/kg material 1.5 to 1.6
5.6
Embodied Energy, MJ/kg 20 to 22
76
Embodied Water, L/kg 48
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 69 to 130
200
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 330
210
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 13 to 21
21
Strength to Weight: Bending, points 14 to 20
20
Thermal Diffusivity, mm2/s 13
3.2
Thermal Shock Resistance, points 11 to 17
14