ASTM A414 Steel vs. ASTM A182 Grade F1
Both ASTM A414 steel and ASTM A182 grade F1 are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is ASTM A414 steel and the bottom bar is ASTM A182 grade F1.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 110 to 180 | |
170 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 15 to 26 | |
22 |
Fatigue Strength, MPa | 140 to 260 | |
220 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 73 | |
73 |
Shear Strength, MPa | 230 to 370 | |
340 |
Tensile Strength: Ultimate (UTS), MPa | 360 to 590 | |
540 |
Tensile Strength: Yield (Proof), MPa | 190 to 350 | |
310 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
250 |
Maximum Temperature: Mechanical, °C | 400 | |
410 |
Melting Completion (Liquidus), °C | 1460 | |
1470 |
Melting Onset (Solidus), °C | 1420 | |
1420 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 49 to 50 | |
50 |
Thermal Expansion, µm/m-K | 13 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.2 to 7.3 | |
7.1 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 to 8.4 | |
8.2 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.2 | |
2.4 |
Density, g/cm3 | 7.8 to 7.9 | |
7.9 |
Embodied Carbon, kg CO2/kg material | 1.5 to 1.6 | |
1.5 |
Embodied Energy, MJ/kg | 20 to 22 | |
20 |
Embodied Water, L/kg | 48 | |
48 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 69 to 130 | |
100 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 330 | |
260 |
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 13 to 21 | |
19 |
Strength to Weight: Bending, points | 14 to 20 | |
19 |
Thermal Diffusivity, mm2/s | 13 | |
13 |
Thermal Shock Resistance, points | 11 to 17 | |
16 |