ASTM B477 Au-Ni-Ag vs. Grade 702C Zirconium
Both ASTM B477 Au-Ni-Ag and grade 702C zirconium are otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ASTM B477 Au-Ni-Ag and the bottom bar is grade 702C zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 95 | |
| 97 |
| Elongation at Break, % | 5.5 to 11 | |
| 13 |
| Poisson's Ratio | 0.41 | |
| 0.34 |
| Shear Modulus, GPa | 34 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 550 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 80 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 270 |
| Thermal Expansion, µm/m-K | 15 | |
| 5.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 6.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.1 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 8.9 | |
| 23 |
| Strength to Weight: Axial, points | 5.0 to 9.0 | |
| 18 |
| Strength to Weight: Bending, points | 6.0 to 8.8 | |
| 19 |
| Thermal Shock Resistance, points | 16 to 28 | |
| 55 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Gold (Au), % | 74.2 to 75.8 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 2.6 to 3.4 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.25 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 21.4 to 22.6 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 94.8 to 100 |
| Residuals, % | 0 to 0.3 | |
| 0 |