ASTM B522 Class I vs. SAE-AISI T1 Steel
ASTM B522 class I belongs to the otherwise unclassified metals classification, while SAE-AISI T1 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is ASTM B522 class I and the bottom bar is SAE-AISI T1 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 96 | |
| 200 |
| Poisson's Ratio | 0.41 | |
| 0.29 |
| Shear Modulus, GPa | 34 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 490 | |
| 770 to 2130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 77 | |
| 240 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1810 |
| Melting Onset (Solidus), °C | 1030 | |
| 1750 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 410 |
| Thermal Expansion, µm/m-K | 15 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 9.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.1 | |
| 12 |
| Stiffness to Weight: Bending, points | 8.9 | |
| 21 |
| Strength to Weight: Axial, points | 4.4 to 7.8 | |
| 23 to 64 |
| Strength to Weight: Bending, points | 5.5 to 8.0 | |
| 20 to 40 |
| Thermal Shock Resistance, points | 13 to 24 | |
| 23 to 64 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.65 to 0.8 |
| Chromium (Cr), % | 0 | |
| 3.8 to 4.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Gold (Au), % | 68 to 70 | |
| 0 |
| Iron (Fe), % | 0 | |
| 73.2 to 77.2 |
| Manganese (Mn), % | 0 | |
| 0.1 to 0.4 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Platinum (Pt), % | 5.0 to 7.0 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0.2 to 0.4 |
| Silver (Ag), % | 23.5 to 26.5 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 17.3 to 18.8 |
| Vanadium (V), % | 0 | |
| 0.9 to 1.3 |
| Residuals, % | 0 to 0.35 | |
| 0 |