AWS BAg-27 vs. S46910 Stainless Steel

AWS BAg-27 belongs to the otherwise unclassified metals classification, while S46910 stainless steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-27 and the bottom bar is S46910 stainless steel.

AWS BAg-27 (P07251) Filler Metal UNS S46910 Stainless Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		88
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.32
Poisson's Ratio		0.28

Shear Modulus, GPa		33
Shear Modulus, GPa		76

Tensile Strength: Ultimate (UTS), MPa		160
Tensile Strength: Ultimate (UTS), MPa		680 to 2470

Thermal Properties

Latent Heat of Fusion, J/g		140
Latent Heat of Fusion, J/g		280

Melting Completion (Liquidus), °C		750
Melting Completion (Liquidus), °C		1460

Melting Onset (Solidus), °C		610
Melting Onset (Solidus), °C		1420

Specific Heat Capacity, J/kg-K		330
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		22
Thermal Expansion, µm/m-K		11

Otherwise Unclassified Properties

Density, g/cm³		8.7
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		25
Embodied Carbon, kg CO₂/kg material		4.1

Embodied Energy, MJ/kg		400
Embodied Energy, MJ/kg		55

Common Calculations

Stiffness to Weight: Axial, points		5.7
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		17
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		5.1
Strength to Weight: Axial, points		24 to 86

Strength to Weight: Bending, points		7.6
Strength to Weight: Bending, points		22 to 51

Thermal Shock Resistance, points		5.9
Thermal Shock Resistance, points		23 to 84

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0.15 to 0.5

Cadmium (Cd), %		12.5 to 14.5
Cadmium (Cd), %		0

Carbon (C), %		0
Carbon (C), %		0 to 0.030

Chromium (Cr), %		0
Chromium (Cr), %		11 to 13

Copper (Cu), %		34 to 36
Copper (Cu), %		1.5 to 3.5

Iron (Fe), %		0
Iron (Fe), %		65 to 76

Manganese (Mn), %		0
Manganese (Mn), %		0 to 1.0

Molybdenum (Mo), %		0
Molybdenum (Mo), %		3.0 to 5.0

Nickel (Ni), %		0
Nickel (Ni), %		8.0 to 10

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0
Silicon (Si), %		0 to 0.7

Silver (Ag), %		24 to 26
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.015

Titanium (Ti), %		0
Titanium (Ti), %		0.5 to 1.2

Zinc (Zn), %		24.5 to 28.5
Zinc (Zn), %		0

Residuals, %		0 to 0.15
Residuals, %		0