AWS BNi-1 vs. AWS BVAg-29
AWS BNi-1 belongs to the nickel alloys classification, while AWS BVAg-29 belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is AWS BNi-1 and the bottom bar is AWS BVAg-29.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 180 | |
73 |
Poisson's Ratio | 0.3 | |
0.37 |
Shear Modulus, GPa | 70 | |
27 |
Tensile Strength: Ultimate (UTS), MPa | 450 | |
180 |
Thermal Properties
Brazing Temperature, °C | 1070 to 1200 | |
710 to 790 |
Latent Heat of Fusion, J/g | 360 | |
120 |
Melting Completion (Liquidus), °C | 1040 | |
710 |
Melting Onset (Solidus), °C | 980 | |
620 |
Specific Heat Capacity, J/kg-K | 500 | |
270 |
Thermal Expansion, µm/m-K | 12 | |
20 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.0 | |
9.7 |
Common Calculations
Stiffness to Weight: Axial, points | 13 | |
4.2 |
Stiffness to Weight: Bending, points | 24 | |
14 |
Strength to Weight: Axial, points | 16 | |
5.2 |
Strength to Weight: Bending, points | 16 | |
7.3 |
Thermal Shock Resistance, points | 15 | |
8.8 |
Alloy Composition
Aluminum (Al), % | 0 to 0.050 | |
0 |
Boron (B), % | 2.8 to 3.5 | |
0 |
Cadmium (Cd), % | 0 | |
0 to 0.0010 |
Carbon (C), % | 0.6 to 0.9 | |
0 to 0.0050 |
Chromium (Cr), % | 13 to 15 | |
0 |
Cobalt (Co), % | 0 to 0.1 | |
0 |
Copper (Cu), % | 0 | |
22.5 to 25.5 |
Indium (In), % | 0 | |
14 to 15 |
Iron (Fe), % | 4.0 to 5.0 | |
0 |
Lead (Pb), % | 0 | |
0 to 0.0020 |
Nickel (Ni), % | 69.8 to 75.7 | |
0 |
Phosphorus (P), % | 0 to 0.020 | |
0 to 0.0020 |
Selenium (Se), % | 0 to 0.0050 | |
0 |
Silicon (Si), % | 4.0 to 5.0 | |
0 |
Silver (Ag), % | 0 | |
60.5 to 62.5 |
Sulfur (S), % | 0 to 0.020 | |
0 |
Titanium (Ti), % | 0 to 0.050 | |
0 |
Zinc (Zn), % | 0 | |
0 to 0.0010 |
Zirconium (Zr), % | 0 to 0.050 | |
0 |
Residuals, % | 0 to 0.5 | |
0 |