AWS BNi-3 vs. R60802 Alloy
AWS BNi-3 belongs to the nickel alloys classification, while R60802 alloy belongs to the otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is AWS BNi-3 and the bottom bar is R60802 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 170 | |
| 98 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 66 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 270 |
| Thermal Expansion, µm/m-K | 10 | |
| 6.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 6.5 |
| Embodied Water, L/kg | 220 | |
| 290 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 8.3 |
| Stiffness to Weight: Bending, points | 22 | |
| 23 |
| Strength to Weight: Axial, points | 14 | |
| 18 |
| Strength to Weight: Bending, points | 15 | |
| 19 |
| Thermal Shock Resistance, points | 17 | |
| 53 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 |
| Boron (B), % | 2.8 to 3.5 | |
| 0 |
| Carbon (C), % | 0 to 0.060 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.050 to 0.15 |
| Cobalt (Co), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.5 | |
| 0.070 to 0.2 |
| Nickel (Ni), % | 90.1 to 93.3 | |
| 0.030 to 0.080 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Selenium (Se), % | 0 to 0.0050 | |
| 0 |
| Silicon (Si), % | 4.0 to 5.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.2 to 1.7 |
| Titanium (Ti), % | 0 to 0.050 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.050 | |
| 97.8 to 98.7 |
| Residuals, % | 0 | |
| 0 to 0.11 |