AWS BVAg-0 vs. EN 1.8936 Steel

AWS BVAg-0 belongs to the otherwise unclassified metals classification, while EN 1.8936 steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-0 and the bottom bar is EN 1.8936 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
190
Poisson's Ratio 0.37
0.29
Shear Modulus, GPa 26
73
Tensile Strength: Ultimate (UTS), MPa 130
600

Thermal Properties

Latent Heat of Fusion, J/g 110
250
Melting Completion (Liquidus), °C 960
1460
Melting Onset (Solidus), °C 960
1420
Specific Heat Capacity, J/kg-K 240
470
Thermal Expansion, µm/m-K 20
13

Otherwise Unclassified Properties

Density, g/cm3 10
7.8

Common Calculations

Stiffness to Weight: Axial, points 3.8
13
Stiffness to Weight: Bending, points 13
24
Strength to Weight: Axial, points 3.4
21
Strength to Weight: Bending, points 5.4
20
Thermal Shock Resistance, points 6.6
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.060
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0 to 0.2
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 0 to 0.050
0 to 0.2
Iron (Fe), % 0
95.5 to 98.9
Lead (Pb), % 0 to 0.0020
0
Manganese (Mn), % 0
1.0 to 1.7
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0
0 to 1.0
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.0020
0 to 0.025
Silicon (Si), % 0
0.1 to 0.6
Silver (Ag), % 99.95 to 100
0
Sulfur (S), % 0
0 to 0.015
Vanadium (V), % 0
0 to 0.2
Zinc (Zn), % 0 to 0.0010
0