AWS BVAg-29 belongs to the otherwise unclassified metals classification, while nickel 908 belongs to the nickel alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BVAg-29 and the bottom bar is nickel 908.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 73
180
Poisson's Ratio 0.37
0.3
Shear Modulus, GPa 27
70
Tensile Strength: Ultimate (UTS), MPa 180
1340

Thermal Properties

Latent Heat of Fusion, J/g 120
290
Melting Completion (Liquidus), °C 710
1430
Melting Onset (Solidus), °C 620
1380
Specific Heat Capacity, J/kg-K 270
460
Thermal Expansion, µm/m-K 20
8.6

Otherwise Unclassified Properties

Density, g/cm3 9.7
8.3

Common Calculations

Stiffness to Weight: Axial, points 4.2
12
Stiffness to Weight: Bending, points 14
23
Strength to Weight: Axial, points 5.2
45
Strength to Weight: Bending, points 7.3
33
Thermal Shock Resistance, points 8.8
61

Alloy Composition

Aluminum (Al), % 0
0.75 to 1.3
Boron (B), % 0
0 to 0.012
Cadmium (Cd), % 0 to 0.0010
0
Carbon (C), % 0 to 0.0050
0 to 0.030
Chromium (Cr), % 0
3.8 to 4.5
Cobalt (Co), % 0
0 to 0.5
Copper (Cu), % 22.5 to 25.5
0 to 0.5
Indium (In), % 14 to 15
0
Iron (Fe), % 0
35.6 to 44.6
Lead (Pb), % 0 to 0.0020
0
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0
47 to 51
Niobium (Nb), % 0
2.7 to 3.3
Phosphorus (P), % 0 to 0.0020
0 to 0.015
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 60.5 to 62.5
0
Sulfur (S), % 0
0 to 0.0050
Titanium (Ti), % 0
1.2 to 1.8
Zinc (Zn), % 0 to 0.0010
0