AWS BVAg-29 vs. C44300 Brass
AWS BVAg-29 belongs to the otherwise unclassified metals classification, while C44300 brass belongs to the copper alloys. They have a modest 24% of their average alloy composition in common, which, by itself, doesn't mean much. There are 15 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is AWS BVAg-29 and the bottom bar is C44300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 73 | |
110 |
Poisson's Ratio | 0.37 | |
0.32 |
Shear Modulus, GPa | 27 | |
41 |
Tensile Strength: Ultimate (UTS), MPa | 180 | |
350 |
Thermal Properties
Latent Heat of Fusion, J/g | 120 | |
180 |
Melting Completion (Liquidus), °C | 710 | |
940 |
Melting Onset (Solidus), °C | 620 | |
900 |
Specific Heat Capacity, J/kg-K | 270 | |
380 |
Thermal Expansion, µm/m-K | 20 | |
20 |
Otherwise Unclassified Properties
Density, g/cm3 | 9.7 | |
8.3 |
Common Calculations
Stiffness to Weight: Axial, points | 4.2 | |
7.2 |
Stiffness to Weight: Bending, points | 14 | |
19 |
Strength to Weight: Axial, points | 5.2 | |
12 |
Strength to Weight: Bending, points | 7.3 | |
13 |
Thermal Shock Resistance, points | 8.8 | |
12 |
Alloy Composition
Arsenic (As), % | 0 | |
0.020 to 0.060 |
Cadmium (Cd), % | 0 to 0.0010 | |
0 |
Carbon (C), % | 0 to 0.0050 | |
0 |
Copper (Cu), % | 22.5 to 25.5 | |
70 to 73 |
Indium (In), % | 14 to 15 | |
0 |
Iron (Fe), % | 0 | |
0 to 0.060 |
Lead (Pb), % | 0 to 0.0020 | |
0 to 0.070 |
Phosphorus (P), % | 0 to 0.0020 | |
0 |
Silver (Ag), % | 60.5 to 62.5 | |
0 |
Tin (Sn), % | 0 | |
0.9 to 1.2 |
Zinc (Zn), % | 0 to 0.0010 | |
25.2 to 29.1 |
Residuals, % | 0 | |
0 to 0.4 |