AWS E308 vs. EN 1.4563 Stainless Steel

Both AWS E308 and EN 1.4563 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E308 and the bottom bar is EN 1.4563 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 40
40
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
80
Tensile Strength: Ultimate (UTS), MPa 620
620

Thermal Properties

Latent Heat of Fusion, J/g 290
310
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1380
1370
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
12
Thermal Expansion, µm/m-K 14
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 16
36
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.2
6.3
Embodied Energy, MJ/kg 46
87
Embodied Water, L/kg 150
240

Common Calculations

PREN (Pitting Resistance) 21
39
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 4.2
3.2
Thermal Shock Resistance, points 16
13

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.020
Chromium (Cr), % 18 to 21
26 to 28
Copper (Cu), % 0 to 0.75
0.7 to 1.5
Iron (Fe), % 62.9 to 72.5
31.6 to 40.3
Manganese (Mn), % 0.5 to 2.5
0 to 2.0
Molybdenum (Mo), % 0 to 0.75
3.0 to 4.0
Nickel (Ni), % 9.0 to 11
30 to 32
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.7
Sulfur (S), % 0 to 0.030
0 to 0.010