MakeItFrom.com
Menu (ESC)

AWS E310Mo vs. ASTM A182 Grade F1

Both AWS E310Mo and ASTM A182 grade F1 are iron alloys. They have 49% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E310Mo and the bottom bar is ASTM A182 grade F1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
22
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 620
540

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
50
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 28
2.4
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 5.1
1.5
Embodied Energy, MJ/kg 71
20
Embodied Water, L/kg 210
48

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
19
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 3.7
13
Thermal Shock Resistance, points 15
16

Alloy Composition

Carbon (C), % 0 to 0.12
0 to 0.28
Chromium (Cr), % 25 to 28
0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 42.8 to 52
97.7 to 98.8
Manganese (Mn), % 1.0 to 2.5
0.6 to 0.9
Molybdenum (Mo), % 2.0 to 3.0
0.44 to 0.65
Nickel (Ni), % 20 to 22
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.75
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.045