AWS E310Nb vs. EN 1.0566 Steel

Both AWS E310Nb and EN 1.0566 steel are iron alloys. They have 51% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E310Nb and the bottom bar is EN 1.0566 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 29
24
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 620
550

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
50
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.3
1.6
Embodied Energy, MJ/kg 76
22
Embodied Water, L/kg 200
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
19
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 3.8
14
Thermal Shock Resistance, points 15
17

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 0 to 0.12
0 to 0.18
Chromium (Cr), % 25 to 28
0 to 0.3
Copper (Cu), % 0 to 0.75
0 to 0.3
Iron (Fe), % 44.1 to 53.3
96.2 to 98.9
Manganese (Mn), % 1.0 to 2.5
1.1 to 1.7
Molybdenum (Mo), % 0 to 0.75
0 to 0.080
Nickel (Ni), % 20 to 22
0 to 0.5
Niobium (Nb), % 0.7 to 1.0
0 to 0.050
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.75
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.0080
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.1