AWS E310Nb vs. EN 1.4509 Stainless Steel

Both AWS E310Nb and EN 1.4509 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E310Nb and the bottom bar is EN 1.4509 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 29
21
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
77
Tensile Strength: Ultimate (UTS), MPa 620
530

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Melting Completion (Liquidus), °C 1410
1440
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 14
25
Thermal Expansion, µm/m-K 14
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 31
13
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 5.3
2.8
Embodied Energy, MJ/kg 76
41
Embodied Water, L/kg 200
120

Common Calculations

PREN (Pitting Resistance) 28
18
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
19
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 3.8
6.8
Thermal Shock Resistance, points 15
19

Alloy Composition

Carbon (C), % 0 to 0.12
0 to 0.030
Chromium (Cr), % 25 to 28
17.5 to 18.5
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 44.1 to 53.3
77.8 to 82.1
Manganese (Mn), % 1.0 to 2.5
0 to 1.0
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 20 to 22
0
Niobium (Nb), % 0.7 to 1.0
0.3 to 1.0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.1 to 0.6