AWS E312 vs. Grade 5 Titanium
AWS E312 belongs to the iron alloys classification, while grade 5 titanium belongs to the titanium alloys. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is AWS E312 and the bottom bar is grade 5 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 25 | |
| 8.6 to 11 |
| Poisson's Ratio | 0.27 | |
| 0.32 |
| Shear Modulus, GPa | 80 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 740 | |
| 1000 to 1190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 410 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1610 |
| Melting Onset (Solidus), °C | 1360 | |
| 1650 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 560 |
| Thermal Expansion, µm/m-K | 15 | |
| 8.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 20 | |
| 36 |
| Density, g/cm3 | 7.7 | |
| 4.4 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 38 |
| Embodied Energy, MJ/kg | 52 | |
| 610 |
| Embodied Water, L/kg | 200 | |
| 200 |
Common Calculations
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 35 |
| Strength to Weight: Axial, points | 27 | |
| 62 to 75 |
| Strength to Weight: Bending, points | 24 | |
| 50 to 56 |
| Thermal Shock Resistance, points | 18 | |
| 76 to 91 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 5.5 to 6.8 |
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.080 |
| Chromium (Cr), % | 28 to 32 | |
| 0 |
| Copper (Cu), % | 0 to 0.75 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 52.3 to 63.5 | |
| 0 to 0.4 |
| Manganese (Mn), % | 0.5 to 2.5 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 0 |
| Nickel (Ni), % | 8.0 to 10.5 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 87.4 to 91 |
| Vanadium (V), % | 0 | |
| 3.5 to 4.5 |
| Yttrium (Y), % | 0 | |
| 0 to 0.0050 |
| Residuals, % | 0 | |
| 0 to 0.4 |