AWS E383 vs. EN 1.0545 Steel

Both AWS E383 and EN 1.0545 steel are iron alloys. They have a modest 36% of their average alloy composition in common, which, by itself, doesn't mean much. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS E383 and the bottom bar is EN 1.0545 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 34
24
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 580
550

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 12
45
Thermal Expansion, µm/m-K 14
12

Otherwise Unclassified Properties

Base Metal Price, % relative 37
2.5
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.4
1.7
Embodied Energy, MJ/kg 89
23
Embodied Water, L/kg 240
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
19
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 3.1
12
Thermal Shock Resistance, points 15
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.015
Carbon (C), % 0 to 0.030
0 to 0.22
Chromium (Cr), % 26.5 to 29
0 to 0.35
Copper (Cu), % 0.6 to 1.5
0 to 0.6
Iron (Fe), % 28.8 to 39.2
95.5 to 99.15
Manganese (Mn), % 0.5 to 2.5
0.85 to 1.8
Molybdenum (Mo), % 3.2 to 4.2
0 to 0.13
Nickel (Ni), % 30 to 33
0 to 0.55
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0
0 to 0.017
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.9
0 to 0.55
Sulfur (S), % 0 to 0.020
0 to 0.030
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0
0 to 0.14