AWS E383 vs. Nickel 30
AWS E383 belongs to the iron alloys classification, while nickel 30 belongs to the nickel alloys. They have 79% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS E383 and the bottom bar is nickel 30.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 210 |
| Elongation at Break, % | 34 | |
| 34 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 80 | |
| 82 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 660 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 320 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1480 |
| Melting Onset (Solidus), °C | 1370 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 12 | |
| 10 |
| Thermal Expansion, µm/m-K | 14 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 60 |
| Density, g/cm3 | 8.1 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 6.4 | |
| 9.4 |
| Embodied Energy, MJ/kg | 89 | |
| 130 |
| Embodied Water, L/kg | 240 | |
| 290 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 20 | |
| 22 |
| Strength to Weight: Bending, points | 19 | |
| 20 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 2.7 |
| Thermal Shock Resistance, points | 15 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.030 |
| Chromium (Cr), % | 26.5 to 29 | |
| 28 to 31.5 |
| Cobalt (Co), % | 0 | |
| 0 to 5.0 |
| Copper (Cu), % | 0.6 to 1.5 | |
| 1.0 to 2.4 |
| Iron (Fe), % | 28.8 to 39.2 | |
| 13 to 17 |
| Manganese (Mn), % | 0.5 to 2.5 | |
| 0 to 0.030 |
| Molybdenum (Mo), % | 3.2 to 4.2 | |
| 4.0 to 6.0 |
| Nickel (Ni), % | 30 to 33 | |
| 30.2 to 52.2 |
| Niobium (Nb), % | 0 | |
| 0.3 to 1.5 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.9 | |
| 0 to 0.8 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.020 |
| Tungsten (W), % | 0 | |
| 1.5 to 4.0 |