AWS E383 vs. C82800 Copper
AWS E383 belongs to the iron alloys classification, while C82800 copper belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS E383 and the bottom bar is C82800 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 120 |
| Elongation at Break, % | 34 | |
| 1.0 to 20 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 80 | |
| 46 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 670 to 1140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 240 |
| Melting Completion (Liquidus), °C | 1420 | |
| 930 |
| Melting Onset (Solidus), °C | 1370 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 12 | |
| 120 |
| Thermal Expansion, µm/m-K | 14 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 6.4 | |
| 12 |
| Embodied Energy, MJ/kg | 89 | |
| 190 |
| Embodied Water, L/kg | 240 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 20 | |
| 21 to 36 |
| Strength to Weight: Bending, points | 19 | |
| 20 to 28 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 36 |
| Thermal Shock Resistance, points | 15 | |
| 23 to 39 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.15 |
| Beryllium (Be), % | 0 | |
| 2.5 to 2.9 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 26.5 to 29 | |
| 0 to 0.1 |
| Cobalt (Co), % | 0 | |
| 0.15 to 0.7 |
| Copper (Cu), % | 0.6 to 1.5 | |
| 94.6 to 97.2 |
| Iron (Fe), % | 28.8 to 39.2 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0.5 to 2.5 | |
| 0 |
| Molybdenum (Mo), % | 3.2 to 4.2 | |
| 0 |
| Nickel (Ni), % | 30 to 33 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.9 | |
| 0.2 to 0.35 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 | |
| 0 to 0.12 |
| Zinc (Zn), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.5 |