AWS E630 vs. Grade 11 Titanium
AWS E630 belongs to the iron alloys classification, while grade 11 titanium belongs to the titanium alloys. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS E630 and the bottom bar is grade 11 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 8.0 | |
| 29 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 76 | |
| 38 |
| Tensile Strength: Ultimate (UTS), MPa | 1040 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 420 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1660 |
| Melting Onset (Solidus), °C | 1380 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 540 |
| Thermal Conductivity, W/m-K | 17 | |
| 22 |
| Thermal Expansion, µm/m-K | 14 | |
| 9.2 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 3.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 7.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 47 |
| Embodied Energy, MJ/kg | 40 | |
| 800 |
| Embodied Water, L/kg | 140 | |
| 470 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 35 |
| Strength to Weight: Axial, points | 37 | |
| 19 |
| Strength to Weight: Bending, points | 29 | |
| 22 |
| Thermal Diffusivity, mm2/s | 4.5 | |
| 8.9 |
| Thermal Shock Resistance, points | 28 | |
| 22 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0 to 0.080 |
| Chromium (Cr), % | 16 to 16.8 | |
| 0 |
| Copper (Cu), % | 3.3 to 4.0 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 71.6 to 75.9 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0.25 to 0.75 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 0 |
| Nickel (Ni), % | 4.5 to 5.0 | |
| 0 |
| Niobium (Nb), % | 0.15 to 0.3 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.18 |
| Palladium (Pd), % | 0 | |
| 0.12 to 0.25 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 98.8 to 99.88 |
| Residuals, % | 0 | |
| 0 to 0.4 |