AWS E630 vs. N08367 Stainless Steel

Both AWS E630 and N08367 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS E630 and the bottom bar is N08367 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 8.0
34
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
80
Tensile Strength: Ultimate (UTS), MPa 1040
740

Thermal Properties

Latent Heat of Fusion, J/g 280
310
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 17
12
Thermal Expansion, µm/m-K 14
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 14
33
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 2.8
6.2
Embodied Energy, MJ/kg 40
84
Embodied Water, L/kg 140
200

Common Calculations

PREN (Pitting Resistance) 18
46
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 37
25
Strength to Weight: Bending, points 29
22
Thermal Diffusivity, mm2/s 4.5
3.2
Thermal Shock Resistance, points 28
17

Alloy Composition

Carbon (C), % 0 to 0.050
0 to 0.030
Chromium (Cr), % 16 to 16.8
20 to 22
Copper (Cu), % 3.3 to 4.0
0 to 0.75
Iron (Fe), % 71.6 to 75.9
41.4 to 50.3
Manganese (Mn), % 0.25 to 0.75
0 to 2.0
Molybdenum (Mo), % 0 to 0.75
6.0 to 7.0
Nickel (Ni), % 4.5 to 5.0
23.5 to 25.5
Niobium (Nb), % 0.15 to 0.3
0
Nitrogen (N), % 0
0.18 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030