AWS ENi-1 vs. EN 1.4415 Stainless Steel
AWS ENi-1 belongs to the nickel alloys classification, while EN 1.4415 stainless steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS ENi-1 and the bottom bar is EN 1.4415 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 200 |
| Elongation at Break, % | 22 | |
| 17 to 20 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 69 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 470 | |
| 830 to 930 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 280 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1460 |
| Melting Onset (Solidus), °C | 1310 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 73 | |
| 19 |
| Thermal Expansion, µm/m-K | 11 | |
| 9.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 19 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 19 | |
| 2.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 13 |
| Density, g/cm3 | 8.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 3.6 |
| Embodied Energy, MJ/kg | 150 | |
| 51 |
| Embodied Water, L/kg | 230 | |
| 120 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 22 | |
| 25 |
| Strength to Weight: Axial, points | 15 | |
| 29 to 33 |
| Strength to Weight: Bending, points | 15 | |
| 25 to 27 |
| Thermal Diffusivity, mm2/s | 19 | |
| 5.1 |
| Thermal Shock Resistance, points | 17 | |
| 30 to 34 |
Alloy Composition
| Aluminum (Al), % | 0 to 1.0 | |
| 0 |
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 11.5 to 13.5 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 0 to 0.75 | |
| 75.9 to 82.4 |
| Manganese (Mn), % | 0 to 0.75 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 1.5 to 2.5 |
| Nickel (Ni), % | 92 to 99 | |
| 4.5 to 6.5 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.3 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.015 |
| Titanium (Ti), % | 1.0 to 4.0 | |
| 0 to 0.010 |
| Vanadium (V), % | 0 | |
| 0.1 to 0.5 |
| Residuals, % | 0 to 0.5 | |
| 0 |