AWS ENi-1 vs. EN 1.5662 Steel
AWS ENi-1 belongs to the nickel alloys classification, while EN 1.5662 steel belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is AWS ENi-1 and the bottom bar is EN 1.5662 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 180 | |
190 |
Elongation at Break, % | 22 | |
20 |
Poisson's Ratio | 0.31 | |
0.29 |
Shear Modulus, GPa | 69 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 470 | |
740 to 750 |
Thermal Properties
Latent Heat of Fusion, J/g | 310 | |
250 |
Melting Completion (Liquidus), °C | 1360 | |
1460 |
Melting Onset (Solidus), °C | 1310 | |
1410 |
Specific Heat Capacity, J/kg-K | 450 | |
470 |
Thermal Expansion, µm/m-K | 11 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 19 | |
8.7 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 19 | |
9.8 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 60 | |
7.5 |
Density, g/cm3 | 8.7 | |
8.0 |
Embodied Carbon, kg CO2/kg material | 11 | |
2.3 |
Embodied Energy, MJ/kg | 150 | |
31 |
Embodied Water, L/kg | 230 | |
63 |
Common Calculations
Stiffness to Weight: Axial, points | 12 | |
13 |
Stiffness to Weight: Bending, points | 22 | |
24 |
Strength to Weight: Axial, points | 15 | |
26 |
Strength to Weight: Bending, points | 15 | |
23 |
Thermal Shock Resistance, points | 17 | |
22 |
Alloy Composition
Aluminum (Al), % | 0 to 1.0 | |
0 |
Carbon (C), % | 0 to 0.1 | |
0 to 0.1 |
Copper (Cu), % | 0 to 0.25 | |
0 |
Iron (Fe), % | 0 to 0.75 | |
88.6 to 91.2 |
Manganese (Mn), % | 0 to 0.75 | |
0.3 to 0.8 |
Molybdenum (Mo), % | 0 | |
0 to 0.1 |
Nickel (Ni), % | 92 to 99 | |
8.5 to 10 |
Phosphorus (P), % | 0 to 0.030 | |
0 to 0.020 |
Silicon (Si), % | 0 to 1.3 | |
0 to 0.35 |
Sulfur (S), % | 0 to 0.020 | |
0 to 0.0050 |
Titanium (Ti), % | 1.0 to 4.0 | |
0 |
Vanadium (V), % | 0 | |
0 to 0.050 |
Residuals, % | 0 to 0.5 | |
0 |