AWS ENi-1 vs. Grade 361 Molybdenum

AWS ENi-1 belongs to the nickel alloys classification, while grade 361 molybdenum belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS ENi-1 and the bottom bar is grade 361 molybdenum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 180
310
Elongation at Break, % 22
6.3
Poisson's Ratio 0.31
0.31
Shear Modulus, GPa 69
120
Tensile Strength: Ultimate (UTS), MPa 470
620

Thermal Properties

Latent Heat of Fusion, J/g 310
370
Specific Heat Capacity, J/kg-K 450
250
Thermal Expansion, µm/m-K 11
7.0

Otherwise Unclassified Properties

Density, g/cm3 8.7
10
Embodied Carbon, kg CO2/kg material 11
28
Embodied Energy, MJ/kg 150
330
Embodied Water, L/kg 230
360

Common Calculations

Stiffness to Weight: Axial, points 12
17
Stiffness to Weight: Bending, points 22
22
Strength to Weight: Axial, points 15
17
Strength to Weight: Bending, points 15
16
Thermal Shock Resistance, points 17
21

Alloy Composition

Aluminum (Al), % 0 to 1.0
0
Carbon (C), % 0 to 0.1
0 to 0.010
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 0 to 0.75
0 to 0.010
Manganese (Mn), % 0 to 0.75
0
Molybdenum (Mo), % 0
99.9 to 100
Nickel (Ni), % 92 to 99
0 to 0.0050
Nitrogen (N), % 0
0 to 0.0020
Oxygen (O), % 0
0 to 0.0070
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 1.3
0 to 0.010
Sulfur (S), % 0 to 0.020
0
Titanium (Ti), % 1.0 to 4.0
0
Residuals, % 0 to 0.5
0