AWS ER70S-A1 vs. Grade 31 Titanium
AWS ER70S-A1 belongs to the iron alloys classification, while grade 31 titanium belongs to the titanium alloys. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AWS ER70S-A1 and the bottom bar is grade 31 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 22 | |
| 20 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 73 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 590 | |
| 510 |
| Tensile Strength: Yield (Proof), MPa | 450 | |
| 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 420 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1660 |
| Melting Onset (Solidus), °C | 1420 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 540 |
| Thermal Conductivity, W/m-K | 50 | |
| 21 |
| Thermal Expansion, µm/m-K | 13 | |
| 8.7 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 3.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 6.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 36 |
| Embodied Energy, MJ/kg | 20 | |
| 600 |
| Embodied Water, L/kg | 48 | |
| 230 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 99 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 540 | |
| 940 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 35 |
| Strength to Weight: Axial, points | 21 | |
| 32 |
| Strength to Weight: Bending, points | 20 | |
| 32 |
| Thermal Diffusivity, mm2/s | 14 | |
| 8.5 |
| Thermal Shock Resistance, points | 17 | |
| 39 |
Alloy Composition
| Carbon (C), % | 0 to 0.12 | |
| 0 to 0.080 |
| Cobalt (Co), % | 0 | |
| 0.2 to 0.8 |
| Copper (Cu), % | 0 to 0.35 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 96.1 to 99.3 | |
| 0 to 0.3 |
| Manganese (Mn), % | 0 to 1.3 | |
| 0 |
| Molybdenum (Mo), % | 0.4 to 0.65 | |
| 0 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.35 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0.3 to 0.7 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 97.9 to 99.76 |
| Residuals, % | 0 | |
| 0 to 0.4 |