AWS ERNiFeCr-2 vs. 50Cr-50Ni-Cb Alloy
AWS ERNiFeCr-2 belongs to the nickel alloys classification, while 50Cr-50Ni-Cb alloy belongs to the otherwise unclassified metals. They have 69% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS ERNiFeCr-2 and the bottom bar is 50Cr-50Ni-Cb alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 28 | |
| 5.6 |
| Poisson's Ratio | 0.29 | |
| 0.26 |
| Shear Modulus, GPa | 75 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 1300 | |
| 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 350 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 480 |
| Thermal Expansion, µm/m-K | 13 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 60 |
| Density, g/cm3 | 8.3 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 13 | |
| 9.2 |
| Embodied Energy, MJ/kg | 190 | |
| 130 |
| Embodied Water, L/kg | 250 | |
| 350 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 43 | |
| 21 |
| Strength to Weight: Bending, points | 32 | |
| 20 |
| Thermal Shock Resistance, points | 38 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 0.2 to 0.8 | |
| 0 to 0.25 |
| Boron (B), % | 0 to 0.0030 | |
| 0 |
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.1 |
| Chromium (Cr), % | 17 to 21 | |
| 47 to 52 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 11.6 to 24.6 | |
| 0 to 1.0 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0 to 0.3 |
| Molybdenum (Mo), % | 2.8 to 3.3 | |
| 0 |
| Nickel (Ni), % | 50 to 55 | |
| 43.3 to 51.6 |
| Niobium (Nb), % | 4.8 to 5.5 | |
| 1.4 to 1.7 |
| Nitrogen (N), % | 0 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0.65 to 1.2 | |
| 0 to 0.5 |
| Residuals, % | 0 to 0.5 | |
| 0 |