AWS ERNiFeCr-2 vs. CC760S Brass

AWS ERNiFeCr-2 belongs to the nickel alloys classification, while CC760S brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiFeCr-2 and the bottom bar is CC760S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 28
22
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 75
42
Tensile Strength: Ultimate (UTS), MPa 1300
180

Thermal Properties

Latent Heat of Fusion, J/g 310
190
Melting Completion (Liquidus), °C 1460
1000
Melting Onset (Solidus), °C 1410
940
Specific Heat Capacity, J/kg-K 450
390
Thermal Conductivity, W/m-K 12
150
Thermal Expansion, µm/m-K 13
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
38
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
40

Otherwise Unclassified Properties

Base Metal Price, % relative 75
28
Density, g/cm3 8.3
8.6
Embodied Carbon, kg CO2/kg material 13
2.6
Embodied Energy, MJ/kg 190
43
Embodied Water, L/kg 250
320

Common Calculations

Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 23
19
Strength to Weight: Axial, points 43
5.8
Strength to Weight: Bending, points 32
8.2
Thermal Diffusivity, mm2/s 3.2
45
Thermal Shock Resistance, points 38
6.2

Alloy Composition

Aluminum (Al), % 0.2 to 0.8
0 to 0.010
Arsenic (As), % 0
0.050 to 0.15
Boron (B), % 0 to 0.0030
0
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 21
0
Copper (Cu), % 0 to 0.3
83 to 88
Iron (Fe), % 11.6 to 24.6
0 to 0.15
Lead (Pb), % 0
0 to 0.5
Manganese (Mn), % 0 to 0.35
0 to 0.1
Molybdenum (Mo), % 2.8 to 3.3
0
Nickel (Ni), % 50 to 55
0 to 0.1
Niobium (Nb), % 4.8 to 5.5
0
Phosphorus (P), % 0 to 0.015
0
Silicon (Si), % 0 to 0.35
0 to 0.020
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.3
Titanium (Ti), % 0.65 to 1.2
0
Zinc (Zn), % 0
10.7 to 17
Residuals, % 0 to 0.5
0