Age Hardened ASTM B540 vs. Aged 300 Maraging Steel
Age hardened ASTM B540 belongs to the otherwise unclassified metals classification, while aged 300 maraging steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is age hardened ASTM B540 and the bottom bar is aged 300 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 1.1 | |
| 6.5 |
| Fatigue Strength, MPa | 350 | |
| 860 |
| Poisson's Ratio | 0.38 | |
| 0.3 |
| Shear Modulus, GPa | 39 | |
| 75 |
| Shear Strength, MPa | 700 | |
| 1190 |
| Tensile Strength: Ultimate (UTS), MPa | 1240 | |
| 2030 |
| Tensile Strength: Yield (Proof), MPa | 1000 | |
| 1990 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 270 |
| Melting Completion (Liquidus), °C | 1220 | |
| 1480 |
| Melting Onset (Solidus), °C | 1020 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 450 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 13 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 | |
| 130 |
| Stiffness to Weight: Axial, points | 4.7 | |
| 13 |
| Stiffness to Weight: Bending, points | 12 | |
| 23 |
| Strength to Weight: Axial, points | 27 | |
| 68 |
| Strength to Weight: Bending, points | 20 | |
| 43 |
| Thermal Shock Resistance, points | 61 | |
| 62 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.050 to 0.15 |
| Boron (B), % | 0 | |
| 0 to 0.0030 |
| Calcium (Ca), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Cobalt (Co), % | 0 | |
| 8.5 to 9.5 |
| Copper (Cu), % | 13.5 to 14.5 | |
| 0 |
| Gold (Au), % | 9.5 to 10.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 65 to 68.4 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 | |
| 4.6 to 5.2 |
| Nickel (Ni), % | 0 | |
| 18 to 19 |
| Palladium (Pd), % | 34 to 36 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Platinum (Pt), % | 9.5 to 10.5 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Silver (Ag), % | 29 to 31 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0.5 to 0.8 |
| Zinc (Zn), % | 0.8 to 1.2 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.020 |
| Residuals, % | 0 to 0.3 | |
| 0 |