Annealed Silver vs. Annealed R60901 Alloy
Both annealed silver and annealed R60901 alloy are otherwise unclassified metals. Both are furnished in the annealed condition. There are 17 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is annealed silver and the bottom bar is annealed R60901 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 71 | |
98 |
Elongation at Break, % | 29 | |
22 |
Poisson's Ratio | 0.37 | |
0.34 |
Shear Modulus, GPa | 26 | |
37 |
Tensile Strength: Ultimate (UTS), MPa | 190 | |
500 |
Thermal Properties
Latent Heat of Fusion, J/g | 110 | |
250 |
Melting Completion (Liquidus), °C | 960 | |
1870 |
Specific Heat Capacity, J/kg-K | 240 | |
270 |
Thermal Conductivity, W/m-K | 420 | |
17 |
Thermal Expansion, µm/m-K | 20 | |
6.3 |
Otherwise Unclassified Properties
Density, g/cm3 | 10 | |
6.6 |
Common Calculations
Stiffness to Weight: Axial, points | 3.8 | |
8.3 |
Stiffness to Weight: Bending, points | 13 | |
23 |
Strength to Weight: Axial, points | 4.9 | |
21 |
Strength to Weight: Bending, points | 6.9 | |
21 |
Thermal Diffusivity, mm2/s | 170 | |
9.7 |
Thermal Shock Resistance, points | 9.5 | |
58 |
Alloy Composition
Niobium (Nb), % | 0 | |
2.4 to 2.8 |
Silver (Ag), % | 99.9 to 100 | |
0 |
Zirconium (Zr), % | 0 | |
96.8 to 97.5 |
Residuals, % | 0 | |
0 to 0.29 |